Hastelloy C22 wire is one of them fabricated with the best raw material. Hastelloy C22 wire is made out of C22 alloy, which is a most multipurpose alloy. It is a composite of nickel, tungsten, molybdenum, and chromium. Due to these elements, components made out of material grade C22 having enhanced resistivity against corrosion and other variety of industrial chemicals.
Nickel, tungsten, molybdenum, and chromium-based alloy made wire are weldable and can easily be formed. So whether you are using a gas tungsten arc, a gas metal arc, a shielded metal arc, this Hastelloy C22 wire can adapt to any manufacturing method. Because it naturally prevents the production of grain boundary precipitates. It’s not always the case with other kinds of alloys. It makes C22 versatile and ideal wire for different situations where irregularly shaped wire is used in areas that would be extremely corrosive for normal wiring.
Hastelloy Alloy C22 Wire which is selected over different alloys for the clamshell bellows after extensive testing. Analysis of corrosion resistance of the tested material can also be performed in Hastelloy C22 Wire and the results provided to the customer as a free technical service. Hastelloy C22 Wire is tested for this hydrofluoric acid pre – scrubber after the original material failed.
Sleeved electro – galvanizing finishing rolls made of Hastelloy C22 Coil Wire are ready for placement in a steel finishing manufacturing line. Conditions were so severe in C-stage bleaching operations at one mill that even Hastelloy C22 Electrode welds were suspect. As a preventive maintenance measure, three millimetres was ground off each weld and replaced with a weld deposit of Hastelloy C22 Electrode. These Alloy C22 Coil Wire helps reduce defects on the rolls which is necessary to produce defect free galvanized steel for the automotive industry.
Alloy C22 Wire had four times better corrosion resistance than the original material and 20 percent better than the other alloys at 150 Degree F to 200 Degree F. Solid rocket propellant effluents and salt air in Alloy C22 Wire causes pitting and crevice corrosion attack of stainless steel. Alloy C22 Wire has a more restricted composition for improved performance, where these improvements are of such significance that it has been widely patented throughout the world.
| UNS No | N06022 |
|---|---|
| Standard | Hastelloy C22 Wires |
| Diameter | 0.1mm to 100mm |
| Length | 100mm to 6000mm, Custom Cut Length |
| Form | Filler Wire, Coil Wire, Wire, etc. |
| GRADE | Werks Toff | UNS | Ni | Cr | Co | Mo | Fe | Cu | Nb | Al | Ti | C | S | Si | Mn | Others |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Hastelloy C22 | 2.4602 | N06022 | Remainder | 20.0 - 22.5 | 2.5 Min | 12.5 - 14.5 | 2.0 - 6.0 | - | - | - | - | 0.015 Max | 0.02 Max | 0.08 Max | 0.50 Max | W - 2.5-3.5 / V - 0.35 Min / P - 0.02 Max |
| Element | Tensile Strength Rm (Mpa) | Yield strength Rp0.2 (Mpa) | Elongation A5% | Density (g/cm3) |
|---|---|---|---|---|
| Hastelloy C22 | 690 | 310 | 45 | 8.69 |
Power Plants Industry
Aerospace Industry
Refineries Industry
Oil & Gas Industry
Sugar Industry
Chemical Industry
Petrochemical Industry